Thank you so much for your comments. It sounds very logical as the probes are indeed the original along with the rest of the insides of this machine (270 hours of on time). The entire module is offset by 50-75 degrees cooler so suspecting that the pe
Electronics Forum | Sun Feb 18 03:27:56 EST 2024 | erikfriesen
You might consider buying a machine on eBay. I found a replacement the other day that came with xp. I think where it gets tricky is if you have the winkic software installed, as it is 16 bit software and seems to break on newer xp versions. There ma
Electronics Forum | Wed Feb 20 16:03:19 EST 2013 | bocci572
I am wondering if anyone has had issues with their Heller oven rails warping. It appears that our 1800EXL and 1900W oven rails sag after time. They eventually contact the safety mesh and then create hestitation of the chain, thus creating defects.
Electronics Forum | Fri Mar 24 15:08:20 EDT 2023 | erikfriesen
The nameplate specs for a 2004 Heller 1088EXL show 240V 60A, and specify Largest Heater Load of 25A. As each of the 8 heater elements is 6000W or 9.5R, how does this really work? Obviously all 8 elements on would pull 200A, so does the machine only
Electronics Forum | Thu Jul 15 22:03:07 EDT 2004 | KEN
In no particular order: Will the failed joints wet when touched with an iron + flux? Is there flux surrounding the joint (post reflow). If no, you may be baking it out premateurely. Is this assembly wave soldered? Where is defect discovered in yo
Electronics Forum | Sun Jan 31 14:03:41 EST 1999 | Dean
| I have a recent design (1 component side only) that calls for 2 surface mounted antenna's (brass plated) to be mounted on a PCB. The problem arises when the PCB is 18x11.25 and has 15 to 20 PCB's in the pallet (IE weight, fixturing to hold the ant
Electronics Forum | Fri Nov 10 17:00:05 EST 2006 | darby
Yep. If speed is not an issue a Heller 1500 will pretty well do you fine unless you are trying to process a brick. A Heller 1700 will not give you any more heated length, so don't get sucked in to that one. However, they are a little more fun to pl
Electronics Forum | Mon Apr 03 01:35:31 EDT 2006 | darby
I have a less than perfectly designed pcb requiring double sided lead free reflow. Several components from either side will detatch using the standard process. If I was using Sn63Pb37 I would just dispense some adhesive after paste and cure at the r
Electronics Forum | Mon Sep 14 20:19:33 EDT 2020 | kumarb
Hi. 1) recommend to phone up Heller for assistance on this case 2) using the wakeup profile, can you confirm if the problem remains or not when you skip the warm up of zone # 2? 3) each zone is based on 2 heaters (this is what we have on our 1809e
Electronics Forum | Tue Oct 01 08:01:23 EDT 2002 | mjz289
WE USE A HELLER 1500 EXL OVEN (5 ZONE OVEN) AND HAVE BEEN DOING PBGAs FROM 292 TO 780 BALLS WITH .O32" PITCH (.8 mm) AND METAL STIFFENERS ON TOP WITH NO PROBLEMS. I AM GETTING 210 - 215 DEGREES C AT THE BGA BALLS WITH 50 - 65 SECONDS ABOVE LIQUIDUS